Effet d’un traitement thermique post-soudage sur le comportement mécanique d’un joint de soudure
Loading...
Files
Date
Journal Title
Journal ISSN
Volume Title
Publisher
Université Ferhat Abbas- Sétif .Institut d’optique et de Mécanique de Précision
Abstract
As part of this research, we examined the mechanical and metallographic behavior of Friction Stir Welding welds carried out on 5086 aluminum alloy plates with a thickness of 5 mm, assembled end to end using a rotational speed. 1400 rpm and a feed speed of 10 mm/min. Post-weld heat treatments were also carried out to improve the mechanical characteristics of the welds. Various characterization techniques, such as tensile and resilience tests, optical microscopy and micro hardness tests, were used. The results demonstrate that samples welded at a rotational speed of 1400 rpm exhibit an optimal balance between mechanical and microstructural properties.
Description
كجزء من هذا البحث، قمنا بفحص السلوك الميكانيكي والمعدني للحام الاحتكاك الذي تم تنفيذه على 5086 لوح من سبائك الألومنيوم بسماكة 5 مم، وتم تجميعها نهاية إلى نهاية باستخدام سرعة الدوران. 1400 دورة في الدقيقة وسرعة تغذية 10 مم/دقيقة. كما تم إجراء المعالجات الحرارية بعد اللحام لتحسين الخصائص الميكانيكية للحامات. تم استخدام تقنيات توصيف مختلفة، مثل اختبارات الشد والمرونة، والمجهر الضوئي، واختبارات الصلابة الدقيقة. أظهرت النتائج أن العينات الملحومة بسرعة دوران تبلغ 1400 دورة في الدقيقة تظهر توازنًا مثاليًا بين الخواص الميكانيكية والبنية المجهرية